Hydrogen Embrittlement Relief (Baking) of Steel Parts

Standard:
Revised:
  • 2001-04-01
 
  • HISTORICAL Access the latest revision: AMS2759/9D
Publisher:
  • SAE International
Pages:
5
Scope:

This specification covers the requirements for embrittlement relief (baking) of heat treated steel parts to remove hydrogen infused during plating and other chemical processing (e.g., stripping, chemical milling, pickling, and etching). This specification is applicable to parts made from carbon, low-alloy, and martensitic stainless steel heat treated to a minimum strength of 180 ksi (1241 MPa) or higher heat treated to a minimum hardness of 40 HRC or equivalent, or harder. It is also applicable to threaded fasteners made from carbon, low-alloy, or martensitic stainless steels heat treated to a minimum strength of 150 ksi (1034 MPa) or 34 HRC or equivalent, parts made from high strength precipitation hardening stainless steels other than A-286, and steel parts which have been case hardened (carburized, nitrided, nitrocarburized, or carbonitrided).

History:
Standard Published Revision Status
AMS2759/9D 2009-05-15 Latest Revised
2007-11-28 Historical Revised
2003-04-30 Historical Revised
2001-04-01 Historical Revised
1996-11-01 Historical Issued
AKA:
  • SAE AMS 2759/9
Sector:
Access
Now
SAE MOBILUS Subscriber? You may already have access.
Buy
Select
Price
List
Download
$76.00
Add
Mail
$76.00
Members save up to 18% off list price.
Grade
If you are currently using this technical report:
Share
HTML for Linking to Page
Page URL

Related Items

Training / Education
2013-04-09
Training / Education
2013-04-09
Training / Education
2013-04-09
Technical Paper / Journal Article
2009-07-12
Technical Paper / Journal Article
2014-04-20
Training / Education
2013-04-09
Training / Education
2013-02-20